High Strength AI-7A77
3D PRINTED ALUMINUM 7A77.60L
| HEAT TREATED MATERIAL PROPERTIES 1,2,3 | Metric | Imperial |
|---|---|---|
| Yield Strength | 490 – 585 MPa | 71 – 85 ksi |
| Ultimate Tensile Strength | 520 – 615 MPa | 75 – 89 ksi |
| Elongation | 6 – 14% | |
| POWDER SIZES |
|---|
| Available Powder D50 values ranging from 20 to 65 μm. |
1 Tensile testing completed in accordance with ASTM E8
2 Ranges depend on processing parameters and post build HIP and heat treatment conditions
3 Recommended Heat Treatment: Hot Isostatic Press (optional): 15-30ksi, 380-420 C, 1-2 hr.
2 Ranges depend on processing parameters and post build HIP and heat treatment conditions
3 Recommended Heat Treatment: Hot Isostatic Press (optional): 15-30ksi, 380-420 C, 1-2 hr.
Solution Treat: 460 – 485C, 1-2 hr, Water quench, Age: 115-130C, 5-24 hr
 |
|
||||||||||||||||